OK 94.25
SMAW
Welding current, A
DC+
|
     |
| Classifications | Approvals | Typical all weld metal composition | Typical properties all weld metal | | | | Mn | <0,5 | | P | <0,1 | | Cu | 92,5 | | Sn | 7,0 | | Fe | <0,2 |
| Redrying temperature, °C
300
Redrying time, hours
2
Recovery
95
Yield stress, MPa
235
Tensile strength, MPa
330-390
Elongation, %
25
Elongation, %
25
Weld metal hardness, a w
95 HB
Machinability
Good
| Charpy V | | Test temps, °C | Impact values, J | | +20 | 25 | | 0 | 20 |
|
| Diameter, mm | 2,5 | 3,2 | 4,0 | | Length, mm | 350 | 350 | 350 | | Arc voltage, V | 22 | 24 | 25 | | Welding current, A | 60-90 | 90-125 | 125-170 | | N. Kg weld metal/kg electrodes | 0,71 | 0,72 | 0,74 | | B. No. of electrodes/kg weld metal | 77,0 | 46,0 | 30,5 | | H. Kg weld metal/hour arc time | 1,2 | 1,9 | 2,9 | | T. Burn-off time, secs/electrode | 39 | 40 | 41 |
|
|