OK 68.53
SMAW
Welding current, A
DC+, AC OCV 60 V
|
      |
| Classifications | Approvals | Typical all weld metal composition | Typical properties all weld metal | | EN 1600 | | E 25 9 4 N L R 3 2 | | Werkstoff Nr. | | (1.4410) |
| | | C | <0,04 | | Si | 0,6 | | Mn | 0,8 | | Cr | 25,2 | | Ni | 9,8 | | Mo | 4,0 | | N | 0,25 |
| Redrying temperature, °C
250
Redrying time, hours
2
Recovery
106
Yield stress, MPa
700
Tensile strength, MPa
850
Elongation, %
30
Elongation, %
30
Ferrite content
FN 35-50
| Charpy V | | Test temps, °C | Impact values, J | | +20 | 50 | | -40 | 40 |
|
| Diameter, mm | 2,5 | 3,2 | 4,0 | | Length, mm | 300 | 350 | 350 | | Arc voltage, V | 22 | 22 | 23 | | Welding current, A | 55-85 | 70-110 | 110-150 | | N. Kg weld metal/kg electrodes | 0,60 | 0,60 | 0,60 | | B. No. of electrodes/kg weld metal | 94 | 47 | 32 | | H. Kg weld metal/hour arc time | 0,9 | 1,2 | 1,7 | | T. Burn-off time, secs/electrode | 43 | 62 | 67 |
|
|