FILARC 88S
SMAW
Welding current, A
DC+/-, AC OCV 65 V
|
      |
| Classifications | Approvals | Typical all weld metal composition | Typical properties all weld metal | | SFA/AWS A5.5 | | E8016-G | | EN ISO 2560-A | | E 50 6 Mn1Ni B 12 H5 |
| | ABS | E8016-G (-60ºC) | |
| DB | 10.105.16 | |
| DNV | 3 YH10 | |
| GL | 6YH10 | |
| LR | 5Y40H15 | |
| VdTÜV | 06107 | |
| CE | EN 13479 | |
| | C | 0,06 | | Si | 0,4 | | Mn | 1,7 | | Ni | 0,8 | | P | ³0,02 | | S | 0,015 | | Cr | ³0,05 | | Mo | ³0,01 | | V | ³0,02 | | Nb | ³0,01 | | Cu | ³0,05 | | Al | 0,008 | | Sn | ³0,01 | | Ti | ³0,03 | | Pb | ³0,01 | | As | ³0,02 | | Sb | ³0,01 |
| Recovery
100%
Yield stress, MPa
>500
Tensile strength, MPa
560-660
Elongation, %
>22
Elongation, %
>22
| Charpy V | | Test temps, °C | Impact values, J | | -20 | 150 | | -40 | 100 | | -60 | 60 |
|
| Diameter, mm | 2,5 | 3,2 | 4,0 | 4,0 | 5,0 | | Length, mm | 350 | 350 | 350 | 450 | 450 | | Arc voltage, V | 21,2 | 21,4 | 21,0 | 21,5 | 22,6 | | Welding current, A | 55-85 | 80-140 | 110-170 | 110-170 | 180-230 | | N. Kg weld metal/kg electrodes | 0,65 | 0,59 | 0,58 | 0,62 | 0,63 | | B. No. of electrodes/kg weld metal | 87,1 | 54,5 | 36,6 | 26,8 | 16,9 | | H. Kg weld metal/hour arc time | 0,7 | 0,96 | 1,2 | 1,27 | 1,95 | | T. Burn-off time, secs/electrode | 59 | 69 | 82 | 106 | 109 |
|
|