FILARC 76S
SMAW
Welding current, A
DC+ -, AC OCV 65 V
|
      |
| Classifications | Approvals | Typical all weld metal composition | Typical properties all weld metal | | SFA/AWS A5.5 | | E7018-G | | EN 499 | | E 42 6 Mn1Ni B 32 H5 |
| | ABS | 3Y (-60ºC) | |
| BV | 3YH5 | |
| DNV | 3 YH5 | |
| GL | 6YH10 | |
| LR | 5Y40MH5 | |
| CE | EN 13479 | |
| | C | 0,06 | | Si | 0,4 | | Mn | 1,6 | | Ni | 0,8 | | P | ³0,02 | | S | 0,015 | | Cr | ³0,05 | | Mo | ³0,01 | | V | ³0,02 | | Nb | ³0,01 | | Cu | ³0,05 | | Al | 0,008 | | Sn | ³0,01 | | Ti | ³0,03 | | Pb | ³0,01 | | As | ³0,02 |
| Recovery
100%
Yield stress, MPa
>460
Tensile strength, MPa
530-640
Elongation, %
>22
Elongation, %
>22
| Charpy V | | Test temps, °C | Impact values, J | | -20 | 150 | | -60 | 60 |
|
| Diameter, mm | 2,5 | 3,0 | 3,2 | 3,2 | 3,5 | 4,0 | 4,0 | 5,0 | | Length, mm | 350 | 350 | 350 | 450 | 350 | 350 | 450 | 450 | | Arc voltage, V | 24 | 21 | 23,8 | 23,6 | 21,6 | 22 | 22,2 | 24,3 | | Welding current, A | 55-85 | 100-125 | 80-140 | 80-130 | 125-175 | 120-180 | 120-170 | 180-270 | | N. Kg weld metal/kg electrodes | 0,65 | 0,63 | 0,57 | 0,62 | 0,61 | 0,63 | 0,61 | 0,62 | | B. No. of electrodes/kg weld metal | 87 | 55 | 54 | 39 | 41 | 31 | 24 | 15 | | H. Kg weld metal/hour arc time | 0,7 | 1,05 | 1,12 | 1,13 | 1,4 | 1,51 | 1,4 | 2,22 | | T. Burn-off time, secs/electrode | 59 | 63 | 60 | 83 | 63 | 78 | 109 | 106 |
|
|