OK 67.66
SMAW
Welding current, A
AC, DC+ OCV 70 V
|
   |
| Classifications | Approvals | Typical all weld metal composition | Typical properties all weld metal | | | | C | <0,03 | | Si | 0,5 | | Mn | 0,1 | | Cr | 23,0 | | Ni | 13,0 | | Mo | <0,5 | | Cu | <0,2 |
| Redrying temperature, °C
250
Redrying time, hours
2
Yield stress, MPa
430
Tensile strength, MPa
580
Elongation, %
45
Elongation, %
45
Ferrite content
FN 4-10
| Charpy V | | Test temps, °C | Impact values, J | | +20 | 70 |
|
| Diameter, mm | 4,0 | | Length, mm | 350 | | Arc voltage, V | 24 | | Welding current, A | 110-150 | | N. Kg weld metal/kg electrodes | 0,58 | | B. No. of electrodes/kg weld metal | 32 | | H. Kg weld metal/hour arc time | 1,7 | | T. Burn-off time, secs/electrode | 65 |
|
|