OK 63.31
SMAW
Welding current, A
AC, DC+ OCV 50 V
|
      |
| Classifications | Approvals | Typical all weld metal composition | Typical properties all weld metal | | SFA/AWS A5.4 | | E316L-17 | | EN 1600 | | E 19 12 3 L R 1 2 | | Werkstoff Nr. | | 1.4430 |
| | DB | 30.039.04 | |
| GL | 4571 | |
| VdTÜV | | |
| CE | EN 13479 | |
| | C | <0,03 | | Si | 0,7 | | Mn | 0,9 | | Cr | 18,5 | | Ni | 11,3 | | Mo | 2,8 | | Cu | <0,3 |
| Yield stress, MPa
460
Tensile strength, MPa
605
Elongation, %
36
Elongation, %
36
Ferrite content
FN 9-12
| Charpy V | | Test temps, °C | Impact values, J | | -60 | 40 |
|
| Diameter, mm | 2,0 | 2,5 | 3,2 | 4,0 | 5,0 | | Length, mm | 300 | 300 | 350 | 350 | 450 | | Arc voltage, V | 26 | 29 | 29 | 29 | 29 | | Welding current, A | 45-65 | 50-90 | 60-120 | 80-170 | 110-240 | | N. Kg weld metal/kg electrodes | 0,57 | 0,56 | 0,56 | 0,56 | 0,57 | | B. No. of electrodes/kg weld metal | 152 | 94 | 50 | 34 | 16 | | H. Kg weld metal/hour arc time | 0,6 | 0,8 | 1,2 | 1,8 | 2,5 | | T. Burn-off time, secs/electrode | 45 | 50 | 64 | 65 | 97 |
|
|