OK 53.35
SMAW


Welding current, A
AC, DC+ OCV 65 V


ClassificationsApprovalsTypical all weld metal compositionTypical properties all weld metal
SFA/AWS A5.1
E7048
CSN 05 5010
E 51.93
DIN 1913
E 51 54 B9
EN ISO 2560-A
E 42 4 B 31 H5
ISO 2560
E 51 5B 56H
ABS3H5, 3Y
BV3 YHH
DB10.039.33
DNV3 YH10
DSEN 499
GL3YH10
LR3, 3Y H15
PRS3 YH10
RS3YHH
SFSEN 499
SSEN 499
Ü10.039/1
VdTÜV 00631
CEEN 13479
C0,06
Si0,5
Mn0,9
P³0,03
S³0,03
Redrying temperature, °C
350
Redrying time, hours
2
Recovery
105%
Yield stress, MPa
460
Tensile strength, MPa
560
Elongation, %
30
Elongation, %
30
Charpy V
Test temps, °CImpact values, J
-20140
-30110
-4090

Diameter, mm3,24,04,55,0
Length, mm 450 450 450 450
Arc voltage, V 25 27 27 28
Welding current, A 80-150 110-200 150-230 170-280
N. Kg weld metal/kg electrodes 0,65 0,70 0,64 0,68
B. No. of electrodes/kg weld metal 38 25,0 20 16,0
H. Kg weld metal/hour arc time 1,37 2,2 2 2,9
T. Burn-off time, secs/electrode 69 69 89 77

 